Dilin 704 Polymer Waxy Colloidal Coatings

Dilin 704 is a two-component solvent-free waxy heavy-duty anticorrosive coating with a solid content of 98%. With wax as the main component and chemical active ingredients and active cage structure particles added, Dilin 704 not only has good flexibility, impact resistance and chemical corrosion resistance, but also has good adhesion on smooth galvanized surface and residual paint surface.
1, the solid content is high, the bottom surface is integrated, the primary coating is thick, and the film is formed by reaction;
2. The coating film has good flexibility, flexibility and impact resistance;
3, a labyrinth channel is formed after curing, which effectively prevents the penetration of media such as water and chloride ions;
4. Excellent corrosion resistance to acid, alkali, salt and other chemicals;
5. Excellent adhesion makes it applicable to various substrate surfaces.
Dilin 704 petroleum equipment, offshore platforms, chemical tanks, pipelines, sewage tanks, steel structures, submerged equipment and facilities and other manufacturing and repair fields. It is suitable for overweight corrosion protection of steel structures and concrete in C4, C5-1, C5-M, Im2 and Im3 environments.

1. Solid content: 98%
2. Specific gravity: 1.35 kg/L.
3. Mixing ratio: A:B = 4:1
4. Theoretical coating rate: 6㎡/kg, 85 μ m. The actual coating rate should consider the appropriate loss.
5. Typical film thickness: 85-170μm for wet film and 50-100μm for dry film.